About this Dataset

Aged And Unaged Ultra High Molar Mass Polyethylene Flexible Unidirectional Composite Laminate Tensile Testing For Soft Body Armor Applications

This dataset contains mechanical testing data at two different loading rates for two different aging conditions (wet and dry at 70 °C) for five different extraction time points for ultra high molar mass polyethylene (UHMMPE) unidirectional (UD) laminate. In each folder there is a spreadsheet (.csv) with the test data collected during loading, and a (.avi) video file for each of the tests done under those conditions.
Organization: Department of Commerce
Last updated: 2025-09-30T04:57:38.126180
Tags: aging, body-armor, laminate, uhmmpe, uhmwpe

Tables

Table 1

@usgov.doc_gov_aged_and_unaged_ultra_high_molar_mass_polyethy_7b0e2801.table_1

110.77 kB
1,182 rows
21 columns

CREATE TABLE table_1 (
  "sheet" VARCHAR  -- Sheet #,
  "location" BIGINT  -- Location #,
  "batch" BIGINT,
  "test_number_within_batch" BIGINT,
  "days_aged" DOUBLE,
  "humid_or_dry" VARCHAR,
  "loading_rate_mm_min" BIGINT  -- Loading Rate (mm/min),
  "unaged_damage_rating" DOUBLE,
  "unaged_damaged_on_front" VARCHAR  -- Unaged Damaged On Front?,
  "unaged_damaged_on_back" VARCHAR  -- Unaged Damaged On Back?,
  "unaged_description_type_and_location_of_damage" VARCHAR  -- Unaged Description ( Type And Location Of Damage),
  "description_of_damage_prior_to_test_after_ageing" VARCHAR  -- Description Of Damage Prior To Test, After Ageing,
  "testing_notes" VARCHAR,
  "faliure_type" VARCHAR,
  "correlated_to_damage" VARCHAR  -- Correlated To Damage?,
  "peak_load_n" DOUBLE  -- Peak Load (N),
  "right_strain_at_break_mm_mm" VARCHAR  -- Right Strain At Break (mm/mm),
  "central_strain_at_break_mm_mm" VARCHAR  -- Central Strain At Break (mm/mm),
  "left_strain_at_break_mm_mm" VARCHAR  -- Left Strain At Break (mm/mm),
  "peak_stress_mpa" DOUBLE  -- Peak Stress (MPa),
  "modulus_gpa" VARCHAR  -- Modulus (GPa)
);